What kind of steel does equivalent material of nm500 steel belong to

Preheating cutting: The most effective way to prevent steel plate cutting cracks is to preheat before cutting. Before flame cutting, the steel plate is usually preheated, and the preheating temperature mainly depends on the quality level and thickness of the steel plate. The preheating method can be carried out with flame burner, electronic heating pad, or heating furnace. In order to determine the preheating effect of the steel plate, the required temperature should be tested at the heating point.

The wear-resistant composite plate, equivalent material of NM500 steel should be pre heat treated to eliminate the residual stress produced in the machining process. If conditions permit, vacuum heating quenching and cryogenic treatment after quenching should be selected as far as possible. On the premise of ensuring the hardness of steel plate, pre cooling, step cooling and quenching or high temperature quenching should be selected as far as possible. For some wear-resistant composite plates, pre heat treatment, aging heat treatment and quenching, tempering and nitriding heat treatment can be used to control the accuracy of the wear-resistant composite plate.

equivalent material of NM500 steel controlled rolling is that, on the basis of adjusting the chemical composition of equivalent material of NM500 steel, by controlling the heating temperature, rolling temperature, deformation system and other process parameters, the change law of austenite structure and the microstructure of phase transformation products are controlled, so as to achieve the purpose of refining the structure and improving the strength and toughness of equivalent material of NM500 steel.

The company strengthens process management and pays attention to assessment. One of the key points of good service is to strengthen the process management and improve the evaluation mechanism. Make the after-sales service system more perfect and provide better service for customers.