element of hardox 400 exported to Malaysia
The company has superior geographical location and convenient transportation. After more than 20 years of market trials and tribulations, from small to large, from weak to strong, in order to meet the needs of customer extension development, the company expanded the deep processing services of cutting steel pieces. Now we have built a business system integrating steel plate, steel plate cutting and steel deep processing. The company provides one-stop solution for customers with lower price, higher quality and faster response speed.element of HARDOX 400
EN10025-2 S355JR low alloy steel grade is equivalent to GB Q345B in Chinese standard. For the normal thickness, these two steel grades are both owned 345MPa yield strength. Plate S355JR+N indicates that the S355JR steel plate must be done Normalized heat treatment when rolling for improve the steel strength and weldability. Our mill would roll element of HARDOX 400, S355JR alloy steel plate under as rolled or control rolled when customers' have not requested any heat treatment in their P/O,element of HARDOX 400.
Element of HARDOX 400,A516 Gr65 steel is a carbon steel plate for medium and low temperature pressure vessels, which implements the ASTM A516 standard. A516 Gr65 plate has the following characteristics: good impact resistance, small temperature deformation, good welding performance, good fatigue resistance, good anti-layered cracking performance, micro-alloying, high purity, low carbon equivalent, strong resistance to sulfur and hydrogen. Our pressure vessel plate has good dimensional tolerance and surface quality.
Element of HARDOX 400,S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.element of HARDOX 400
API 5L X52 steel with the thickness range is 1.2-40mm, the width range is 1220-4200mm, and the length range is 5000-18000mm. API 5L X52 steel’s mechanical properties is the yield strength 300MPa, and the tensile strength 460MPa. To be specified in details: Maximum content for C≤0.28%, Mn≤1.4%, P≤0.030%, S is 0.030%, V+Nb+Ti≤0.15%, Copper maximum is 0.50%, nickel maximum 0.50%, chromium 0.50%, Molybdenum 0.15%.
The company focuses on two markets at home and abroad, and has a group of 56 experienced sales elites and professional and technical personnel It can provide customers with drawing design, deep processing services and installation solutions 20 years of project experience has provided high-quality carbon steel, alloy steel products and high-quality after-sales service to customers in many countries around the world The company has won widespread praise from customers,element of HARDOX 400.