hardox 500 equivalent for general intermediate strength applications

Quenching is a heat treatment process in which steel parts are heated to above the critical temperature, and after proper heat preservation, the parts are quickly cooled to room temperature in water or oil, so that martensite transformation occurs. The hardness of the quenched HARDOX 500 equivalent increases sharply. Quenching is to prepare the organization for adjusting and improving the performance of HARDOX 500 equivalent during tempering, while tempering determines the performance and life of the workpiece.

When the HARDOX 500 equivalent, wear-resistant steel plate is produced, relevant heat treatment must be carried out, and then forging and processing are carried out after preheating. When the wear-resistant steel plate is heat treated, the temperature should be properly controlled. The heating temperature of the wear-resistant steel plate is 810-830 degrees, and the holding time depends on the furnace loading method. Tempering temperature: 320 degrees, sufficient time is necessary, oil cooling after tempering to reduce temper brittleness.

2020 October HARDOX 500 equivalent specification: 8*2200*10000, 16*2150*10400, 30*2500*6200, 31.2*2950*9380, 7*2200*8000, 30*2200*10000, 14*2400*9900, 18.5*2700*9570, 21*2100*8810, 14*2070*9060, 12*2200*10000, 14*1950*8000, 36*2200*7700, 7*2200*8000, 14*2070*9060, 10*2200*8000, 20*2500*10000, 14*2400*10000, 30*2000*7400, 6*2800*12000, 21*2100*8810, 32*2200*10000, 16*2150*10250, 27*2500*9000, 20*2100*7000, 21*2100*9100.

Steel material has an irreplaceable role in many projects, especially in building construction, bridge cofferdams, road construction, foundation pit support, garden engineering, excavator paving, subgrade engineering and other projects. Therefore, the quality of HARDOX 500 equivalent steel material can not be ignored, so how should customers identify the authenticity of steel when choosing steel materials? Today we would like to analyze it together. So that it can help you to purchase satisfied steel materials in the future.